号数	ばね論文集 65 号（ 2020 年）
ページ数	pp.15-19
種類	論文
論文名	鋼製圧縮コイルばねの擬弾性残留変位のSi 組成および磁場依存性
Title	Effect of Si Content and Magnetic Field to Anelastic Residual Displacement of Steel Compression Coil Spring
著者	小竹茂夫1)，佐野祐太2)
Author	Shigeo KOTAKE1), Yuuta SANO2)
抄録	We measured the temporal change of residual displacement immediately after unloading at room temperature for three compression coil springs, SWP-B, DASH and SWOSC-V, with different Si compositions. All the total residual displacement of the compression coil spring changed logarithmically with time, and the total residual displacement increased with the compression holding time. Also, in the pearlite steel springs, the larger the Si composition, the smaller the total residual displacement. However,high-silicon oil-tempered steel spring, SWOSC-V, showed some increase of the total residual displacement.Furthermore, the total residual displacement became smaller under the magnetic eld. These results suggest that the magnetic domain wall may be involved in the pinning of dislocations in the residual displacement.
Abstract	我々は，Si組成の異なるSWP-B，DASHおよびSWOSC-Vからなる3種類の圧縮コイルばねについて，室温下で除荷直後の残留変位の時間変化を測定した．その結果，これらの圧縮コイルばねの残留変位は，時間に対して対数関数的に変化し，その全残留変位は，圧縮保持時間とともに増加した．またパーライト鋼線圧縮コイルばねは，Si組成の大きくなるほど，概全残留変位は小さくなった．しかしながら，高いSiを含むオイルテンパー鋼線圧縮コイルばねは，多少，全残留変位が増加した．さらに，パーライト鋼線やオイルテンパー鋼線からなる圧縮コイルばねの全残留変位は，磁場下で小さくなった．これらの結果から，残留変位における転位のピン止めには，磁壁が関与している可能性があると考えられる．
著者の所属	1)三重大学 大学院 2)三重大学
Belonging	1)Mie University, Graduate School 2)Mie University
Key Words	Compression coil spring, Anelasticity, Si content, Magnetic eld, Dislocation, Pinning